CÔNG NGHỆ TẠO KEO MELAMINE UREA FORMALDEHYDE (MUF) CHO SẢN XUẤT VÁN DÁN THÂN THIỆN MÔI TRƯỜNG ĐÁP ỨNG TIÊU CHUẨN XUẤT KHẨU (CARB - P2/ E0 /F***/ F****)
Keywords:
Adhesive synthesis process,, Melamine Urea Formaldehyde (MUF) adhesive, free formaldehyde content,, plywood, CARB -P2/E0/F***/F**** standardAbstract
As derived from the practical requirements of the industry for exporting
plywood with super low free formaldehyde emissions, it must be less then
0.04 - 0.07ppm corresponding to the levels of CARB - P2/E0/F****,
according to the regulations of US, Europe and Japan; Researching on
synthesis technology of Melamine Urea Formaldehyde (MUF) wood
adhesive to evaluate the impact of changing toward reducing the mole ratio
of Formaldehyde to Urea + Melamine (F/U+M), while increasing melamine
content in industrial production process (scale of 3,000 kg/batch) to free
formaldehyde content of the adhesive and plywood product. The research
results showed that the MUF glue product, used for plywood production, to
reach super low free formaldehyde content of the plywood at 0.03 -0.06ppm. The plywood was made with high mechanical strength properties:
modulus of rupture MOR = 70 Mpa, modulus of elasticity MOE = 10,234
Mpa, swelling coeficient is as low as 6.5% and the adhesion strength meet
Class 1 according to EN 314 - 1 & 2. Applying the synthesized MUF
adhesive produced succesfully plywood, which meet the export standards
to for major export markets of Vietnam such as: USA, EU and Japan
References
1. Cơ sở hóa học các hợp chất cao phân tử, 1997. Nhà xuất bản Khoa học và Kỹ thuật Hà Nội.
2. Dyana J Merline, Sulafudin Vukusic and Ahmed A Abdala, 2013. Melamine formaldehyde: curing studies and reaction mechanism. The Society of Polymer Science, Japan (SPSJ). Polymer Journal (2013) 45.
3. Hse, C. Y; Fu, F.; Pan, H., 2008. Melamine -modified urea formaldehyde resin for bonding particle boards. ForestProd J, 58, 56.
4. Joakim Jeremejeff, 2012. Investigation of UF-resins - the Effect of the Formaldehyde/Urea Molar Ratio during Synthesis. Master of Science Thesis, Stockholm, Sweden.
5. Lars Kloeser, Ursula Kües, Christian Schöpper, Hossein Hosseinkhani, Stefan Schütze, Sebastian Dantz, Ithzaz Malik, Hubert Vos, Michael Bartholme, Cora Müller, Andrea Polle and Alireza Kharazipour, 2007. Panel Boards and Conventional Adhesives. In book: Wood production, wood technology, and biotechnological impacts. Chapter: Panel Boards and Conventional Adhesives. Publisher: Universitätsverlag Göttingen, Editors: Ursula Kües.
6. Mary Lillian Boyd, 1945. Kinetic studies on the formation of hexamine. Doctoral thesis, Faculty of Graduate Studies and Research o£ McGill University.
7. Nguyễn Hồng Minh và Trần Đức Trung, 2021. Ảnh hưởng của tỷ lệ các thành phần nguyên liệu đến chất lượng keo Melamine Urea Formaldehyde cho sản xuất ván dán chống ẩm và thân thiện môi trường. Tạp chí Khoa học Lâm nghiệp, ISSN: 1859 - 0373, Số 1 - 2021, trang 100 - 110.
8. Nguyễn Hồng Minh và Tạ Thị Thanh Hương, 2021. Quy trình công nghệ tổng hợp keo urea formaldehyde biến tính melamine (MUF - E1. M13) cho sản xuất ván dán chống ẩm và thân thiện môi trường. Tạp chí Nông nghiệp
và Phát triển nông thôn, ISSN: 1859 - 4581, Số 401 năm 2021, trang 105 - 112.
9. Paiva, N. T., Pereira, J., Ferra, J. M., Crsuz, P., Carvalho, L. and Magalhães, F. D., 2012. Study of influence of synthesis condition on properties of melamine-urea formaldehyde resins.
10. Thông tư số 16/2022/TT-BNNPTNT của Bộ Nông nghiệp và Phát triển nông thôn: Ban hành Quy chuẩn kỹ thuật quốc gia về keo dán gỗ QCVN 03 - 01:2022/BNNPTNT: Quy chuẩn kỹ thuật quốc gia về keo dán gỗ.
11. QCVN 03-01-2002/BNNPTNT: Quy chuẩn kỹ thuật quốc gia về keo dán gỗ
12. Tiến bộ kỹ thuật đối với sản phẩm keo Melamine Urea Formaldehyde (MUF-E1. M13) dùng cho sản xuất ván dán theo Quyết định Số: 417 /QĐ-TCLN-KH&HTQT, ngày 24 tháng 12 năm 2020.
13. Zhang, J., Wang, X., Zhang, S., Gao, Q., and Li, J., 2013. ”Effects of melamine addition stage on performance and curing behavion of melamine urea formaldehyde MUF resin,” BioResources 8 (4), 550 0 - 5514. DOI: 1 015 376 /biore.8.4.5500 - 5514.