Assessment the bonding levels of Eucalyptus camaldulensis by using synteko 1985 (EPI 1985/1993
Keywords:
Eucalyptus camandulensis,, fast growing tree, forest, shear strengthAbstract
The bonding properties of Eucalyptus camaldulensis 14 year old in Dai Lai with popular wood adhesive Emulsion Polymer Isocyanate (EPI 1985/1993) were experimented in two conditions including dry and wet environments. The results of bonding strength test were good and exceed those of Acacia and Meliaceae species with the former being over 14 MPa, the later being 11 MPa and 10 MPa, repectively.
Although the bonding levels of treated samples were smaller than those of untreated samples, this deviance is insignificant at approximately 4 MPa. In addition, the difference between dry and wet conditions was also a little. This was shown that as using EPI 1985/1993 adhesive in bonding of Eucalyptus camaldulensis wood component bars ensured the required quality, even if in the E environment has the impacts of water immersion and drying process
References
1. Đỗ Văn Bản, 2011. Nghiên cứu một số giải pháp công nghệ làm giảm nứt vỡ gỗ Bạch đàn trắng (Eucalyptus camaldulensis Dehnh.) ở Việt Nam để sản xuất gỗ xẻ cho đồ mộc thông dụng. Đề tài tiến sĩ. Viện Khoa học Lâm nghiệp Việt Nam.
2. Phạm Văn Chương và Nguyễn Hữu Quang, 2003. Công nghệ sản xuất ván nhân tạo - Tập 1. NXB Nông nghiệp, Hà Nội.
3. Nguyễn Trọng Nghĩa, 2010. Nghiên cứu và xác định trị số ép hợp lý khi dán dính gỗ Keo lá tràm khi sử dụng chất kết dính Synteko 1980/1993 và Synteko 1985/1993. Luận văn tốt nghiệp. Trường Đại học Lâm nghiệp Việt
Nam.
4. Lê Xuân Tình, 1998. Khoa học gỗ. NXB Nông nghiệp.
5. Tiêu chuẩn Quốc gia Việt Nam, 2010. TCVN 8577:2010. Kết cấu gỗ - gỗ ghép thanh bằng keo - Phương pháp thử tách mạch keo